Deformation-induced microstructural changes in Fe40Ni40P14B6 metallic glass

Published online by Cambridge University Press:  31 January 2011

G.J. Fan,
M. X. Quan,
Z. Q. Hu,
W. Löser and
J. Eckert
G.J. Fan
Affiliation:
State Key Laboratory for RSA, Institute of Metal Research, Chinese Academy of Science, Shenyang 110015, China, and IFW Dresden, Institute of Metallic Materials, 01171 Dresden, Germany
M. X. Quan
Affiliation:
State Key Laboratory for RSA, Institute of Metal Research, Chinese Academy of Science, Shenyang 110015, China
Z. Q. Hu
Affiliation:
State Key Laboratory for RSA, Institute of Metal Research, Chinese Academy of Science, Shenyang 110015, China
W. Löser
Affiliation:
IFW Dresden, Institute of Metallic Materials, 01171 Dresden, Germany
J. Eckert
Affiliation:
IFW Dresden, Institute of Metallic Materials, 01171 Dresden, Germany
Get access

Abstract

The effect of mechanical deformation via high-energy ball milling on the structure of the Fe40Ni40P14B6 metallic glass was studied by means of x-ray diffactometry, transmission electron microscopy (TEM), and differential scanning calorimetry (DSC). After 5 h of milling, TEM observations indicated that some nanocrystallites with a diameter of about 6 nm precipitated from surface layers of the amorphous ribbons, whereas the bulk remained amorphous. When milling time was increased to 11 h, bulk crystallization occurred. The amorphous Fe40Ni40P14B6 alloy crystallized into a mixture of γ–(Fe, Ni) and (Fe, Ni)3(P, B). To understand the microstructural changes occurring in the amorphous ribbons before the onset of bulk crystallization, the isothermal crystallization behavior of as-deformed amorphous ribbons was studied. Compared with as-quenched amorphous ribbons, the local value of the Avrami exponent, derived from isothermal DSC data, increased from 3.5 to 4.1 for bulk crystallization. The thermal crystallization mechanism of deformed amorphous Fe40Ni40P14B6 ribbons changed from an eutectic-type reaction with simultaneous precipitation of γ–(Fe, Ni) and (Fe, Ni)3(P,B) from the amorphous matrix to a primary-type reaction with precipitation of α–Fe(P,B) preceding the formation of γ–(Fe,Ni) and (Fe,Ni)3(P,B). Our results suggest that several hours of mechanical milling cause surface crystallization and some atomic rearrangements in the amorphous alloy. The latter effect may be responsible for the observed primary-type reaction for crystallization of the deformed amorphous alloy

Information

Type
Articles
Information
Journal of Materials Research , Volume 14 , Issue 9 , September 1999, pp. 3765 - 3774
Copyright
Copyright © Materials Research Society 1999

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Article purchase

Temporarily unavailable

References

REFERENCES

1.Johnson, W.L., Prog. Mater. Sci. 30, 81 (1986).CrossRefGoogle Scholar
2.Masumoto, T. and Maddin, R., Mater. Sci. Eng. 19, 1 (1975).CrossRefGoogle Scholar
3.Davies, H.A. and Small, C.J., J. Less-Common Met. 140, 185 (1988).CrossRefGoogle Scholar
4.Pampillo, C.A., Scripta Metall. 6, 915 (1972).CrossRefGoogle Scholar
5.Chen, H.S., Leamy, H.J., and O'Brien, H.J., Scripta Metall. 7, 115 (1973).Google Scholar
6.Spaepen, F., Acta Metall. 25, 407 (1977).CrossRefGoogle Scholar
7.Donovan, P.E. and Stobbs, W.M., Acta Metall. 29, 1419 (1981).CrossRefGoogle Scholar
8.Chen, H., He, Y., Shiflet, G.J., and Poon, S.J., Nature 367, 541 (1994).CrossRefGoogle Scholar
9.Trudeau, M.L., Schulz, R., Dussault, D., and Van Neste, A., Phys. Rev. Lett. 64, 99 (1990).CrossRefGoogle Scholar
10.Bansal, C., Fultz, B., and Johnson, W.L., Nanostruct. Mater. 4, 919 (1994).CrossRefGoogle Scholar
11.Fan, G.J., Song, X.P., Quan, M.X., and Hu, Z.Q., Nanostruct. Mater. 5, 433 (1995).CrossRefGoogle Scholar
12.He, Y., Shiflet, G.J., and Poon, S.J., Acta Metall. Mater. 43, 83 (1995).CrossRefGoogle Scholar
13.Huang, B-H., Perez, R.J., Crawford, P.J., Nutt, S.R., and Lavernia, E.J., Nanostruct. Mater. 7, 57 (1996).CrossRefGoogle Scholar
14.Fan, G.J., Quan, M.X., Hu, Z.Q., Li, Y.L., and Liang, Y., Appl. Phys. Lett. 68, 915 (1996).CrossRefGoogle Scholar
15.Walter, J.L., Bartram, S.F., and Russell, R.R., Met. Trans. 9A, 803 (1978).CrossRefGoogle Scholar
16.Watanabe, T. and Scott, M., J. Mater. Sci. 15, 1131 (1980).CrossRefGoogle Scholar
17.Morris, D.G., Acta Metall. 29, 1213 (1981).CrossRefGoogle Scholar
18.Avrami, M., J. Chem. Phys. 7, 1103 (1939);CrossRefGoogle Scholar
Avrami, M., J. Chem Phys. 8, 212 (1940);CrossRefGoogle Scholar
Avrami, M., J. Chem. Phys. 9, 177 (1941).CrossRefGoogle Scholar
19.Calka, A. and Radlinski, A.P., J. Mater. Res. 3, 59 (1988).CrossRefGoogle Scholar
20.Ranganathan, S. and von Heimendahl, M., J. Mater. Sci. 16, 2401 (1981).CrossRefGoogle Scholar
21.Fan, G.J., Quan, M.X., and Hu, Z.Q., Appl. Phys. Lett. 68, 319 (1996).CrossRefGoogle Scholar
22.Fan, G.J., Quan, M.X., and Hu, Z.Q., J. Appl. Phys. 80, 6055 (1996).CrossRefGoogle Scholar
23.Eckert, J., Schultz, L., Hellstern, E., and Urban, K., J. Appl. Phys. 64, 3224 (1988).CrossRefGoogle Scholar
24.Schwarz, R.B. and Koch, C.C., Appl. Phys. Lett. 49, 146 (1986).CrossRefGoogle Scholar
25.Pearson, W.B., A Handbook of Lattice Spacings and Structures of Metals and Alloys, edited by Raynor, G.V. (Pergamon Press, Inc. New York, 1976), p. 639.Google Scholar
26.Miyoshi, K. and Buckley, D.H., Thin Solid Films 118, 363 (1984).CrossRefGoogle Scholar
27.Fan, G.J., Quan, M.X., and Hu, Z.Q., Appl. Phys. Lett. 68, 1159 (1996).CrossRefGoogle Scholar