Dimensional changes in highly oriented pyrolytic graphite due to electron-irradiation

Published online by Cambridge University Press:  03 March 2011

J. Koike and
D.F. Pedraza
J. Koike
Affiliation:
Oregon State University, Corvallis, Oregon 97331-6001
D.F. Pedraza
Affiliation:
Oak Ridge National Laboratory, P.O. Box 2003, Oak Ridge, Tennessee 37831-7274
Get access

Abstract

One of the main problems found in the nuclear applications of graphite is its dimensional instability under irradiation, involving both swelling and shape changes. In order to understand better the mechanisms that give rise to these changes, highly oriented pyrolytic graphite was irradiated with 300 keV electrons at temperatures between 25 and 657 °C in a transmission electron microscope (TEM). Microscopic dimensional changes and structural disordering were studied in directions parallel and perpendicular to the graphite basal plane. Changes in the specimen length were investigated by measuring the distance between two markers on the specimen surface in TEM images. Changes in the lattice parameter and the crystalline structure were studied by a TEM diffraction technique. In agreement with reported results, large increases in the specimen length and the lattice parameter were observed along the c-axis direction, whereas a relatively small decrease was observed along the a-axis. In irradiation studies conducted at room temperature, it was found that the dimensional change saturates at high dose, at an elongation along the c-axis direction of about 300%. High resolution microscopy revealed that the microstructure had become nanocrystalline. Electron energy loss spectroscopy results showed that the volume change was recovered at this stage. These observations are discussed in terms of point defect evolution and its effects on the microstructure of irradiated graphite.

Information

Type
Articles
Information
Journal of Materials Research , Volume 9 , Issue 7 , July 1994, pp. 1899 - 1907
Copyright
Copyright © Materials Research Society 1994

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Article purchase

Temporarily unavailable

References

REFERENCES

1Salamanca-Riba, L., Braunstein, G., Dresselhaus, M. S., Gibson, J. M., and Endo, M., Nucl. Instrum. Methods, Phys. Res. B 7/8, 487 (1985).CrossRefGoogle Scholar
2Shimizu, H., Suginuma, S., and Gotoh, Y., J. Nucl. Mater. 176–177, 1000 (1990).Google Scholar
3Tanabe, T., Muto, S., Gotoh, Y., and Niwase, K., J. Nucl. Mater. 175, 258 (1990).CrossRefGoogle Scholar
4Gotoh, Y., Shimizu, H., and Murakami, H., J. Nucl. Mater. 162164, 851 (1989).CrossRefGoogle Scholar
5Matsunaga, A., Kinoshita, C., Nakai, K., and Tomokiyo, Y., J. Nucl. Mater. 179–181, 457 (1991).CrossRefGoogle Scholar
6Tanabe, T., Muto, S., and Niwase, K., Appl. Phys. Lett. 61, 1638 (1992).CrossRefGoogle Scholar
7Koike, J. and Pedraza, D. F., in Beam-Solid Interactions: Fundamentals and Applications, edited by Nastasi, M. A., Harriot, L., Herbots, N., and Averback, R. S. (Mater. Res. Soc. Symp. Proc. 279, Pittsburgh, PA, 1993), p. 67.Google Scholar
8Koike, J. and Pedraza, D. F., in International Conf. on Beam Processing of Advanced Materials, edited by Singh, J. and Copley, S.M. (The Minerals, Metals and Materials Society, Warrendale, PA, 1993), p. 519.Google Scholar
9Endo, M., Salamanca–Riba, L., Dresselhaus, G., and Gibson, J. M., J. Chimie Phys. 81, 803 (1984).CrossRefGoogle Scholar
10Dresselhaus, M. S. and Kalish, R., Ion Implantation in Diamond, Graphite and Related Materials (Springer-Verlag, Berlin, Germany, 1992).CrossRefGoogle Scholar
11Annis, B. K., Pedraza, D. F., and Withrow, S. P., J. Mater. Res. 8, 2587 (1993).CrossRefGoogle Scholar
12Kelly, B. T., Physics of Graphite (Applied Science Publishers, London and New Jersey, 1981).Google Scholar
13Elman, B. S., Dresselhaus, M. S., Dresselhaus, G., Maby, E. W., and Mazurek, H., Phys. Rev. B 24, 1027 (1981).CrossRefGoogle Scholar
14Hembree, D. Jr., Pedraza, D. F., Romanoski, G., Withrow, S. P., and Annis, B. K., in Beam-Solid Interactions: Fundamentals and Applications, edited by Nastasi, M. A., Harriot, L., Herbots, N., and Averback, R. S. (Mater. Res. Soc. Symp. Proc. 279, Pittsburgh, PA, 1993), p. 15.Google Scholar
15Kelly, B. T., J. Nucl. Mater. 172, 237 (1990).CrossRefGoogle Scholar
16Thrower, P. A. and Mayer, R. M., Phys. Status Solidi A 47, 11 (1978).CrossRefGoogle Scholar
17Martin, D. G. and Henson, R. W., Philos. Mag. 9, 659 (1964).CrossRefGoogle Scholar
18Pedraza, D. F. and Rifkin, J. A., unpublished.Google Scholar
19Kenik, E. A., Pedraza, D. F., and Withrow, S. P., Proceedings of the 51st Annual Meeting of the Microscopy Society of America (1993), p. 1106.Google Scholar
20Pedraza, D. F., in Phase Formation and Modification by Beam-Solid Interactions, edited by Was, G. S., Rehn, L. E., and Follstaedt, D. M. (Mater. Res. Soc. Symp. Proc. 235, Pittsburgh, PA, 1992), p. 437.Google Scholar
21Simmons, J. H. W., Radiation Damage in Graphite (Pergamon Press, Oxford, 1965).CrossRefGoogle Scholar
22Bell, J. C., Bridge, H., Cottrell, A. H., Greenough, G. B., Reynolds, W. N., and Simmons, J. H. W., Philos. Trans. Roy. Soc. A254, 361 (1962).Google Scholar