CulnSe2 and Other Chalcopyrite-Based Solar Cells

Published online by Cambridge University Press:  29 November 2013

Hans-W. Schock
Get access

Extract

CuInSe2 and related chalcopyrite semiconductors are among the compound semiconductors that have been considered for thin solar cells for about the past 20 years. Recently, high efficiencies close to 17% have been achieved. This result could be the starting point for a new category of solar cells—high-performance thin-film cells—that would combine the high performance of single-crystal cells with possible low-cost thin-film processing.

The development of CuInSe2 cells started in 1974, when single-crystal cells with an efficiency of 12% were reported by a group at Bell Laboratories. Soon after, thin-film solar cells were demonstrated by Kazmerski et al. CuInSe2 thin films have been deposited by evaporating the CuInSe2 source material to completion and adding Se from a separate source. It was found that straight-forward evaporation of the compound does not generally lead to films with stoichiometric composition. By coevaporation of the elements, films with any desired composition can be obtained, provided there is appropriate process control. A “bilayer” recipe developed by Boeing, namely combining Cu-rich films and In-rich films, solved the problem of combining larger grains with suitable electronic properties. By this method, the first CuInSe2 thin-film solar cells with an efficiency exceeding 10% conversion efficiency were fabricated.

Alloying CuInSe2 with CuGaSe2 and CuInS2 considerably increases the potential for the innovative development of solar cells from these materials. The energy gaps covered by these alloys range from about 1 eV to about 2.4 eV The possibility of increasing the energy gap and achieving absorber layers with graded bandgaps has many advantages for the application of these materials in thin-film solar cell modules.

Information

Type
Materials for Photovoltaics
Information
MRS Bulletin , Volume 18 , Issue 10 , October 1993, pp. 42 - 44
Copyright
Copyright © Materials Research Society 1993

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Article purchase

Temporarily unavailable

References

1.Hedström, J., Ohlsén, H., Bodegard, M., Kylner, A., Stolt, L., Hariskos, D., Ruckh, M., and Schock, H-W., Proc. 23rd IEEE Photovoltaics Specialists Conf. (1993) in press.Google Scholar
2.Shay, J.L., Wagner, S., Kasper, H.M., Appl. Phys. Lett. 27 (2) (1975) p. 89.CrossRefGoogle Scholar
3.Kazmerski, L.L., White, F.R., and Morgan, G.K., Appl. Phys. Lett. 29 (1976) p. 268.CrossRefGoogle Scholar
4.Mickelsen, R.A. and Chen, W.S., Proc. 16th IEEE Photovoltaics Specialists Conf. (IEEE, New York, 1982) p. 781.Google Scholar
5.Walter, T., Ruckh, M., Velthaus, K.O., and Schock, H-W., Proc. 11th EC Photovoltaics Solar Energy Conf. (Harwood Academy Publ., 1992) p. 124.Google Scholar
6.Tarrant, D. and Ermer, J., Proc. 23rd IEEE Photovoltaics Specialists Conf. (1993) in press.Google Scholar
7.Fearheiley, M.L., Sol. Cells 16 (1986) p. 91.CrossRefGoogle Scholar
8.Parthé, E., in Ternary and Multinary Compounds, edited by Deb, S.K. and Zunger, A. (Mater. Res. Soc. Symp. Proc., TMC, Pittsburgh, PA, 1987) p. 3.Google Scholar
9.Neumann, H., Nowak, E., and Kühn, G., Cryst. Res. Technol. 16 (12) (1981) p. 1369.CrossRefGoogle Scholar
10.Rincon, C. and Wasim, S.M., in Ternary and Multinary Compounds, edited by Deb, S.K. and Zunger, A. (Mater. Res. Soc. Symp. Proc., TMC, Pittsburgh, PA, 1987) p. 443.Google Scholar
11.Niemi, E. and Stolt, L., in Polycrystallinc Semiconductors II, edited by Werner, J.H. and Strunk, H.P. (Springer Proc. in Physics 54, Springer-Verlag, Berlin, 1991) p. 445.CrossRefGoogle Scholar
12.Schmid, D., Ruckh, M., Grunwald, F., and Schock, H-W, J. Appl. Phys. 73 (6) (1993) p. 2902.CrossRefGoogle Scholar
13.Klenk, R., Walter, T., Schock, H-W., and Cahen, D., Adv. Mater. 5 (2) (1993) p. 114.CrossRefGoogle Scholar
14.Schock, H-W., Burgelman, M., Carter, M., Stolt, L., and Vedel, J., Proc. 11th EC Photovoltaics Solar Energy Conf. (Harwood Academy Publ., 1992) p. 116.Google Scholar
15.Mickelsen, R.A., Chen, W.S., Stanbery, B.J., Dursch, H., Stewart, J.M., Hsiao, Y.R., and Devaney, W., Proc. 18th IEEE Photovoltaics Specialists Conf. (IEEE, New York, 1985) p. 1049.Google Scholar
16.Basol, B.M., Kapur, V.K., Halani, A., Minnick, A., and Leidholm, C., Proc. 23rd IEEE Photovoltaics Specialists Conf. (1993) in press.Google Scholar
17.Kessler, J., Ruckh, M., Hariskos, D., Rühle, U., Menner, R., and Schock, H-W., Proc. 23rd IEEE Photovoltaics Specialists Conf. (1993) in press.Google Scholar
18.Kessler, J., Velthaus, K.O., Ruckh, M., Laichinger, R., Schock, H-W., Lincot, D., Ortega, R., and Vedel, J., Proc. 6th Int. Photovoltaics Sci. Eng. Conf. (PVSEC-6), New Delhi (1992) p. 1005.Google Scholar
19.Chen, W.S., Stewart, J.M., Mickelsen, R.A., and Stanbery, B.J., Proc. 23rd IEEE Photovoltaics Specialists Conf. (1993) in press.Google Scholar
20.Frederic, C., Willett, D., and Tarrant, D., Proc. 23rd IEEE Photovoltaics Specialists Conf. (1993) in press.Google Scholar
21.Zweibel, K., Ullal, H.S., von Roedern, B., Noufi, R., Coutts, T.J., Al-Jassim, M.M., Proc. 23rd IEEE Photovoltaics Specialists Conf. (1993) in press.Google Scholar