Low Temperature Growth of Silicon Structures for Application in Flash Memory Devices
Published online by Cambridge University Press: 01 February 2011
Abstract
An in-depth study of the structural and electrical properties of silicon (Si) films deposited by a novel low temperature technique at temperatures less than 400°C in a 13.56 MHz RF PECVD reactor is reported. The method is based on substrates having to undergo some initial preparatory steps (IPS) before the deposition of Si films in the PECVD chamber. The optical band gap of Si films deposited using this novel technique narrowed to 1.25 eV from 1.78 eV using the traditional a-Si:H deposition recipe. No annealing of any form was performed on the films to attain this band gap. Furthermore, photosensitivities for these films under various deposition conditions were of order 100 compared to 104 for a-Si:H films deposited under like conditions. Using metal-insulator-semiconductor devices, the Si films grown by this novel technique exhibit charge storage and memory behaviour unlike their amorphous counterparts. However, device endurance has been found to be inadequate, probably due to the presence of some contaminants - notably interstitial oxygen - which has been found elsewhere to have adverse effects on the electrical characteristics of Si films. If well harnessed, we suggest Si structures grown by this novel growth technique could be well-suited for flash memory applications, particularly 3-D flash which requires process temperatures to be less than 400 °C.
Information
- Type
- Research Article
- Information
- Copyright
- Copyright © Materials Research Society 2010
References
1
Greg Atwood; Future directions and challenges for ETox Flash memory scaling, IEEE Transactions on Device Materials Reliability Volume 4, (2004), pp. 3001–305Google Scholar
2
Park, D., Kim, K., Ryu, B.I.; “3-D nano-CMOS transistors to overcome scaling limits” in Proc. Solid-state and Integr. Circuits Technol. (2004), 1, 34–35
Google Scholar
3
Koliopoulou, S., Dimitrakis, P., Goustouridis, D., Normand, P., Pearson, C., Petty, M.C., Radamson, H. and Tsoukalas, D., Microelectronic Engineering, 83, (2006), 1563
10.1016/j.mee.2006.01.235Google Scholar
4
Tsuchiya, R., Izawa, M., Kimura, S., “Prospects of Si semiconductor devices and manufacturing technologies in nanometer era”, Hitachi Review (2006), 55(2), 46–55
Google Scholar
6
Mih, T.A., Cross, R.B., Paul, S.; “A novel method for the growth of low temperature polycrystalline silicon for 3–D flash memory” in Materials and Technologies for 3–D Integration, edited by Roozeboom, F., Bower, C., Garrou, P., Koyanagi, M., Ramm, P. (Mater. Res. Soc. Symp. Proc. Volume 1112, Warrendale, PA, 2009) pp1112, 265–269Google Scholar
7
Langfold, A. A., Fleet, M. L., Nelson, B. P. and Marley, M.; “Infrared absorption strength and hydrogen content of hydrogenated amorphous silicon” Phys. Rev. B, (1992), 45, 13367
Google Scholar
8
Müllerová, J., Jureèka, S. and Šutta, P.; “Optical characterization of polysilicon thin films for solar applications”, Solar Energy (2006), 80, 667–674
Google Scholar
9
Hiraki, A.; “Impurity effects” in Amorphous semiconductor Technologies and Devices, edited by Yamakawa, Y., (Japan Annual Reviews in Electronics, Computers and Telecommunication Volume 16, North Holland
1984), pp.134–148
Google Scholar
10
Torres, P., Meier, J., Flückiger, R., Kroll, U., Selvan, J. A. Anna, Keppner, H., and Shah, A.; “Device grade microcrystalline silicon owing to reduced oxygen contamination”, Appl. Phys.Lett., (1996), 69(10), 1373–1375
Google Scholar