High Dielectric Constant Polymer Ceramic Composites

Published online by Cambridge University Press:  10 February 2011

Y. Bai,
V. Bharti,
Z.-Y. Cheng,
H. S. Xu and
Q. M. Zhang
Y. Bai
Affiliation:
Materials Research Laboratory, Pennsylvania State University, University Park. PA 16802
V. Bharti
Affiliation:
Materials Research Laboratory, Pennsylvania State University, University Park. PA 16802
Z.-Y. Cheng
Affiliation:
Materials Research Laboratory, Pennsylvania State University, University Park. PA 16802
H. S. Xu
Affiliation:
Materials Research Laboratory, Pennsylvania State University, University Park. PA 16802
Q. M. Zhang
Affiliation:
Materials Research Laboratory, Pennsylvania State University, University Park. PA 16802
Get access

Abstract

A new polymer-ceramic composite, using the newly developed relaxor ferroelectric polymer that has a high room temperature dielectric constant as the matrix, is reported. Different kinds of ceramic powders were studied and homogeneous composite thin films (20μm) were fabricated. It was observed that the increase of the dielectric constant of the composites with the ceramic content could be described quite well by the expression developed by Yamada et al., when the ceramic content is below 60% by volume. The experimental data shows that the relative dielectric constant of composites using PMN-PT powders can reach more than 250 with weak temperature dependence (i.e., the dielectric constant changes little in a broad temperature range). In addition to high permittivity, the composite prepared in clean environment also has high breakdown field strength (120MV/m), which yields an energy storage density more than 14J/cm3. The dielectric behavior of the composite at various frequencies was also studied and the results show that the material is promising for high frequency applications.

Information

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 600: Symposium FF – Electroactive Polymers , 1999, 281
Copyright
Copyright © Materials Research Society 2000

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Article purchase

Temporarily unavailable

References

1. Dias, C. J., and Das-Gupta, D. K., in FerroelectricP olymer and Ceramic-Polymer Composites, pp. 217–248, edited by Das-Gupta, D. K., Trans-Tech Publications (1994).Google Scholar
2. Dias, C. J., and Das-Gupta, D. K., IEEE Trans. Electr. Insul., Vol.3(5), pp. 706–734 (1996).10.1109/94.544188Google Scholar
3. Hanner, K. A., Safari, A., Newnham, R. E., and Runt, J., Ferroelectrics, 100, pp. 255–260 (1989).10.1080/00150198908007920Google Scholar
4. Gregorio, R. Jr., Cestari, M., and Bernardino, F. E., J. Mater. Sci., 31, p2925–2930 (1996).10.1007/BF00356003Google Scholar
5. Chan, H. L. W., Chan, W. K., Zhang, Y., and Choy, C. L., IEEE Trans. Electr. Insul., Vol.5(4), pp. 505–512 (1998).10.1109/94.708265Google Scholar
6. Newnham, R. E., Ann. Rev. Mater. Sci., 16, p. 47–68 (1986).Google Scholar
7. Wolak, J., IEEE Trans. Electr. Insul., Vol.28(1), pp. 116–121 (1993).Google Scholar
8. Zhang, Q. M., Bharti, V., and Zhao, X., Science, 280, p. 2101–2104 (1998).Google Scholar
9. Yamada, T., Ueda, T., and Kitayama, T., J. Appl. Phys., 53(4), pp. 4328–4332 (1982).Google Scholar
10. Das-Gupta, D. K., Ferroelectrics, 118, pp. 165–189 (1991).Google Scholar
11. Furukawa, T., Ishida, K., and Fukada, E., J. Appl. Phys., 50(7), pp. 4904–4912 (1979).Google Scholar
12. Gao, J., Zheng, L., Zeng, J., and Lin, C., Jpn. J. Appl. Phys., 37, pp. 5126–5127 (1998).Google Scholar
13. Das-Gupta, D. K., and Zhang, R., Ferroelectrics, 134, pp. 71–79 (1992).Google Scholar