Macroporous Materials with Uniform Pores by Emulsion Templating

Published online by Cambridge University Press:  10 February 2011

A. Imhof and
D. J. Pine
A. Imhof
Affiliation:
Department of Chemical Engineering and Department of Materials, University of California, Santa Barbara, California 93106–5080.
D. J. Pine
Affiliation:
Department of Chemical Engineering and Department of Materials, University of California, Santa Barbara, California 93106–5080.
Get access

Abstract

A method was developed for the production of macroporous oxide materials by using the droplets of a nonaqueous emulsion as the templates around which material is deposited through a sol-gel process. Moreover, uniform pores arranged in regular arrays can be obtained by starting with an emulsion of uniform droplets. These droplets first self-assemble into a colloidal crystal after which gelation of the suspending sol-gel mixture captures the ordered structure. After drying and calcination pellets are obtained which contain ordered arrays of spherical pores left behind by the emulsion droplets. The method can be used to make uniform pores in the range from 0.05–5 micrometers in many different materials. We demonstrate the process for titania, silica, and zirconia.

Information

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 497: Symposium Z – Recent Advances in Catalytic Materials , 1997, 167
Copyright
Copyright © Materials Research Society 1998

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Article purchase

Temporarily unavailable

References

REFERENCES

1. Kresge, C.T., Leonowicz, M.E., Roth, W.J., Vartuli, J.C., and Beck, J.S., J. Am. Ceram. Soc. 114, 10834 (1992).Google Scholar
2. Huo, Q., Margolese, D.I., Ciesla, U., Feng, P., Gier, T.E., Sieger, P., Leon, R., Petroff, P.M., Schüth, F., and Stucky, G.D., Nature 368, 317 (1994).Google Scholar
3. Wu, M., Fujiu, T., and Messing, G.L., J. Non-Cryst. Solids 121, 407 (1990).Google Scholar
4. Downs, R.L., Ebner, M.A., and Milner, W.J. in Sol-Gel Technology for Thin Films. Fibers. Preforms. Electronics and Specialty Shapes, edited by Klein, L.C. (Noyes Publications, Park Ridge, NJ, 1988, pp. 330–381.Google Scholar
5. Yablonovitch, E., J. Opt. Soc. Am. B 10, 283 (1993).Google Scholar
6. Photonic Band Gap Materials, edited by Soukoulis, C. (Kluwer, Dordrecht, 1996).10.1007/978-94-009-1665-4Google Scholar
7. Bibette, J., J. Colloid Interface Sci. 147, 474 (1991).10.1016/0021-9797(91)90181-7Google Scholar
8. See e.g. Pusey, P.N. and van Megen, W., Nature 320, 340 (1986).Google Scholar
9. Imhof, A. and Pine, D.J., J. Colloid Interface Sci. 192, 368 (1997).Google Scholar
10. Dinsmore, A.D., Yodh, A.G., and Pine, D.J., Nature 383, 239 (1996).10.1038/383239a0Google Scholar
11. van Blaaderen, A., Ruel, R., and Wiltzius, P., Nature 385, 321 (1997).Google Scholar