Microstructural Characterisation of Microwave Sintered Silicon Nitride Ceramics

Published online by Cambridge University Press:  25 February 2011

Kevin P. Plucknett and
David S. Wilkinson
Kevin P. Plucknett
Affiliation:
Dept. of Materials Science and Engineering, McMaster University, Hamilton, Ontario, Canada
David S. Wilkinson
Affiliation:
Dept. of Materials Science and Engineering, McMaster University, Hamilton, Ontario, Canada
Get access

Abstract

The microstructure of a series of microwave sintered silicon nitride based ceramics have been assessed using a combination of optical microscopy/image analysis and analytical electron microscopy. Materials were studied as-received and after post-sinter hot-isostatic pressing. The grain size of microwave sintered materials was appreciably finer than conventionally processed ceramics of similar composition, although the mechanism involved is not clear. The as-received ceramics exhibited a reverse porosity gradient (with the highest porosity level at the surface) due to heat dissipation to the cooler surroundings during sintering. This also resulted in a small increase in the β′ grain aspect ratio close to the surface arising from an increase in the glass phase viscosity as the temperature decreases. Post-sinter HIPing of microwave sintered samples resulted in the elimination of most of the bulk porosity, but not near the surface. This is due to the reverse porosity gradient previously described, which leads to a transition from closed to open porosity with decreasing density near to the surface.

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Article purchase

Temporarily unavailable

References

REFERENCES

1. Tiegs, T.N., Kiggans, J.O. and Kimrey, H.D., Ceram. Eng. Sci. Proc., 12 1981–1992 [9-10] (1991).Google Scholar
2. Tiegs, T.N., Kiggans, J.O. and Kimrey, H.D., pp. 267–272 in Microwave Processing of Materials II, Materials Research Society, Pittsburgh, PA, 1990.Google Scholar
3. Patterson, M.C.L., Apte, P.S., Kimber, R.M. and Roy, R., pp. 33–36 in Proc. Int. Conf. on Microwaves and High Frequency, Nice, France, 1991.Google Scholar
4. Patterson, M.C.L., Apte, P.S., Kimber, R.M. and Roy, R., pp. 301–310 in Microwave Processing of Materials III, Materials Research Society, Pittsburgh, PA, 1993.Google Scholar
5. Patterson, M.C.L., Apte, P.S., Kimber, R.M. and Roy, R., pp. 291–300 in Microwave Processing of Materials III, Materials Research Society, Pittsburgh, PA, 1993.Google Scholar
6. Meek, T.T., Blake, R.D. and Petrovic, J.J., Ceram. Eng. Sci. Proc., 8 [7-8] 861–871 (1987).Google Scholar
7. Janney, M.A. and Kimrey, H.D., pp. 919–924 in Ceramic Powder Science II, American Ceramic Society, Westerville, OH, 1988.Google Scholar
8. Apte, P.S., Kimber, R.M. and Patterson, M.C.L., pp.167–174 in Structural Ceramics Processing, Microstructure and Properties, Riso National Laboratory, Roskilde, Denmark, 1990.Google Scholar
9. Katz, J.D., Blake, R.D., Petrovic, J.J. and Sheinberg, H., pp. 219–226 in Microwave Processing of Materials I, Materials Research Society, Pittsburgh, PA, 1988.Google Scholar
10. Holcombe, C.E., Meek, T.T. and Dykes, N.L., pp.227–234 in Microwave Processing of Materials I, Materials Research Society, Pittsburgh, PA, 1988.Google Scholar
11. Apte, P.S., Kimber, R.M., Patterson, M.C.L., Roy, R.Y., Mitchell, D.N., International Patent Application No. WO 91/05747 (21d May 1991).Google Scholar
12. Zeigler, G. and Wötting, G., Int. J. High Tech. Ceram., 1 31 (1985).Google Scholar
13. Plucknett, K.P. and Lewis, M.H., Ceram. Eng, Sci. Proc., 12 [7-8] 1327–1344 (1991).Google Scholar
14. Chen, I-W. and Hwang, S.-L., J. Am. Ceram. Soc., 75 [5] 1073–1079 (1992).Google Scholar
15. Wu, X. and Chen, I-W., J. Am. Ceram. Soc., 75 [10] 2733–2741 (1992).Google Scholar
16. Oyama, Y. and Kamigaito, O., Japan. J. Appi. Phys., 10[11]1637 (1971).Google Scholar
17. Plucknett, K.P. and Wilkinson, D.S., Presentation No. 13-SX-92 at the 94th American Ceramic Society Annual Meeting, Minneapolis, MN, April 1992.Google Scholar
18. Patterson, M.C.L., Personal Communication.Google Scholar
19. Wötting, G., Kanka, B. and Ziegler, G., pp. 83–96 in Non-Oxide Technical and Engineering Ceramics, Elsevier, London, England, 1986.Google Scholar
20. Bonnell, D.A., pp. 877–882 in Ceramic Microstructures '86: Role of Interfaces, Materials Science Research, Vol. 21, Plenum Press, New York, 1987.Google Scholar