Using X-ray diffraction for studying the effect of modulation and machining parameters on deformation level in brass particulate produced by modulation assisted machining

Published online by Cambridge University Press:  14 November 2013

Ravinder Singh Joshi and
Harpreet Singh
Ravinder Singh Joshi*
Affiliation:
School of Mechanical, Materials and Energy Engineering, Indian Institute of Technology Ropar, Rupnagar, Punjab, India
Harpreet Singh
Affiliation:
School of Mechanical, Materials and Energy Engineering, Indian Institute of Technology Ropar, Rupnagar, Punjab, India
*
a) Corresponding author email: ravindersj@iitrpr.ac.in

Abstract

Core share and HTML view are not available for this content. However, as you have access to this content, a full PDF is available via the 'Save PDF' action button.

In present investigation, effect of modulation and machining parameters on deformation level of the chips produced during modulation assisted machining (MAM) has been studied. It is shown that disruption in tool-chip contact during modulation assisted machining helps in the formation of discrete chips. Size and shape of the particles produced in MAM can be controlled by varying modulation and machining conditions. Particulates of different shapes and sizes ranging from 100 µm to 5 mm with an aspect ratio of ~10 were produced using MAM. The morphology of the particulates produced was characterized by scanning electron microscope (SEM). Deformation in chip particulates was investigated using X-Ray diffraction. The crystallite size and internal strain in particulates were evaluated using Scherrer and Williamson-Hall methods respectively. The crystallite size of the particulates was found to decrease with decrease in their size, whereas internal strain in particulates was observed to increase with decrease in their size. Furthermore, the length of particulates was observed to decrease with an increase in the ratio of frequency of modulation (fm) to frequency of workpiece rotation (fw). However, the corresponding change in microstrain and crystallite size was insignificant with change in this ratio.

Keywords

Modulation assisted machiningParticulate productionX-Ray diffractionCrystallite sizeMicrostrain

Information

Type
Technical Articles
Information
Powder Diffraction , Volume 28 , Supplement S2 , September 2013, pp. S315 - S326
Copyright
Copyright © International Centre for Diffraction Data 2013 

References

Biju, V., Sugathan, N., Vrinda, V. and Salini, S. (2008). “Estimation of lattice strain in nanocrystalline silver from X-ray diffraction line broadening,” J.Mater. Sci. 43(4): 1175–1179.CrossRefGoogle Scholar
Joshi, R. S. and Singh, H. (2011). “Piezoelectric transducer based devices for development of a sustainable machining system - A review,” Applications of Ferroelectrics. International Symposium 2011 (ISAF/PFM) (and 2011 International Symposium on Piezoresponse Force Microscopy and Nanoscale Phenomena in Polar Materials).Google Scholar
Lemine, O. M. (2009). “Microstructural characterisation of nanoparticles using, XRD line profiles analysis, FE-SEM and FT-IR,” Superlattices Microstruct. 45(6), 576–582.CrossRefGoogle Scholar
Lenel, F. V. (1980). Powder Metallurgy: Principles and Applications, (Metal Powder Industries Federation, Princeton, NJ).Google Scholar
Lonardelli, I., Almer, J., Ischia, G., Menapace, C. and Molinari, A. (2009). “Deformation behavior in bulk nanocrystalline-ultrafine aluminum: in situ evidence of plastic strain recovery,” Scr. Mater. 60(7), 520–523.CrossRefGoogle Scholar
Mann, J. B., Chandrasekar, S. and Compton, W. D. (2009). Tool Holder Assembly and Method for Modulation-Assisted Machining. US Patent no 7,587, 965 B2.Google Scholar
Mann, J. B., Saldana, C., Chandrasekar, S., Compton, W. D. and Trumble, K. P. (2007). “Metal particulate production by modulation-assisted machining.” Scr. Mater. 57(10): 909–912.CrossRefGoogle Scholar
Pourghahramani, P., Altin, E., Mallembakam, M. R., Peukert, W. and Forssberg, E. (2008). “Microstructural characterization of hematite during wet and dry millings using Rietveld and XRD line profile analyses,” Powder Technol. 186(1), 9–21.CrossRefGoogle Scholar
Sánchez, L. C., Arboleda, J. D., Saragovi, C., Zysler, R. D. and Barrero, C. A. (2007). “Magnetic and structural properties of pure hematite submitted to mechanical milling in air and ethanol,” Phys. B (Amsterdam, Neth.) 389(1), 145–149.CrossRefGoogle Scholar
Ungar, T., J., Gubicza, J., Ribarik, G. and Borbely, A. (2001). “Crystallite size distribution and dislocation structure determined by diffraction profile analysis: principles and practical application to cubic and hexagonal crystals,” Journal Appl. Crystallogr. 34(3), 298–310.CrossRefGoogle Scholar
Williamson, G. K. and Hall, W. H. (1953). “X-Ray Line Broadening from Filed Aluminium and Wolfram,” Acta Metall. 1, 22–31.CrossRefGoogle Scholar