Montmorillonites saturated with Li+, Na+, K+, NH4+, Mg2+, Ca2+, Ba2+, or Ni2+ ions can form complexes with propylene carbonate (PC) by intercalation; the d(001) of montmorillonite expands to 19 Å. In the infrared absorption spectra of these complexes, the C=0 stretching band of the intercalated PC molecules shifts to lower frequencies, and the amount of the shift increased with the increase of the polarizing power of the interlayer cations. Water molecules were strongly bound to the cations. The PC molecules interacted with the cations by way of H2O molecules. With the removal of H2O, the PC molecules directly coordinate to the cations and the PC molecules show a much larger red-shift in the C=O frequency. The PC-montmorillonite complexes exhibited osmotic swelling, even in aqueous electrolyte solutions. This finding is interpreted in terms of the formation of thick electric double-layers consisting of PC and H2O between the 2:1 layers.

The rheological behavior of concentrated lateritic suspensions from Cuba is affected by mineral composition and particle size. Electrophoretic mobility and yield stress were considered. The lateritic samples were found to be mostly composed of mixtures of serepentine and goethite in varying proportions. The flow properties of the lateritic suspensions are strongly affected by the mineral composition and particle size. This result was determined by comparison of flow properties of the bulk sample and the colloidal fraction. The electrokinetic curves suggest that heterocoagulation is present in all samples, with a zeta potential minimum at the isoelectric point (IEP), which varies with the serpentine to goethite ratio. A relationship between yield stress (τ0) and the sample volume fraction (ϕ) and particle size (d) was obtained at the IEP from the expression τ0 = kϕ3/d0.5, with the constant k dependent on the sample serpentine to goethite ratio.

Intercalation of amino acids into 10.0-Å hydrated kaolinite was studied by powder X-ray diffraction (XRD), differential thermal analysis-thermal gravimetry (DTA-TG), and infrared (IR) spectroscopy. Intercalation was found to be dependent on the chain-length, pH, and the concentration of the amino acid zwitterion. Near the isoelectric point, fully intercalated phases were obtained in solutions of concentration >0.5–1 M for glycine (Gly), 2–3 M for β-alanine (β-Ala), and 12 M for both γ-aminobutyric acid (γ-Aba) and δ-aminovaleric acid (δ-Ava). ∊-aminocaproic acid (∊-Aca) with a long chain (C = 6) was only partially intercalated. Intercalated amino acid formed a mono-molecular arrangement with the alkyl chain tilting toward the layer at an angle related to H2O content. The compositions of the intercalates of the Gly and β-Ala are Al2Si2O5(OH)4·(Gly)0.67·0.24H2O and Al2Si2O5(OH)4·(β-Ala)0.63·0.25H2O, respectively, based on TG data. From IR data, Gly and β-Ala molecules are found intercalated as zwitterions and these molecules form hydrogen bonds with both the Al-OH and Si-O surfaces of kaolinite. Washing the intercalate with water produced a hydrated kaolinite, which may form a second amino-acid intercalate of high order. Thus, hydrated kaolinite intercalates or deintercalates amino acids depending on concentration and conditions.

A new osmotic-swelling system for montmorillonite with formamide (FA) is described. Water and a variety of polar organic liquids were used to swell FA-montmorillonite complexes. The post-swelling behavior of the complex is interpreted in terms of the bi-functionality of FA as an electron donor/acceptor and the magnitude of the donor number (DN) of the polar liquid relative to that of FA. The FA-montmorillonite complex shows limited swelling of d(001) <2.3 nm for polar liquids with DNs larger than that of FA. In contrast, the FA-montmorillonite complex shows osmotic swelling when the DN of the polar liquid is smaller than that of FA.

A series of hydrothermal experiments were performed to determine the phase relations on the beidellite-saponite pseudo-binary join. Quenched glasses with stoichiometric dehydrated compositions of an Na-rich smectite on the join were heated at 250–500°C for durations of 1–151 d at 100 MPa. Time-temperature diagrams showed that immiscibility occurs between dioctahedral smectite (beidellite) and trioctahedral smectite (saponite) below 400°C. Thus, smectite with intermediate chemical composition was considered as metastable in this system. Above 400°C the assemblage of regularly interstratified saponite-chlorite, quartz, and feldspar was recognized in the intermediate chemical compositional region of this join. On the beidellite side of this join, beidellite and mixed-layer phases of smectite and a regular interstratification of montmorillonite-beidellite, are possible phases that occur at <300°C. They readily reacted to form a mixture of dioctahedral rectorite plus quartz at 300°C. This assemblage then reacted to a dioctahedral “mica”, which can expand with glycol and quartz. On the saponite side of this join, a single phase, saponite, existed at <400°C, and transformed to saponite plus trioctahedral rectorite with aging and increasing temperature of synthesis. The alteration was affected strongly by the chemical composition of the binary system.

Halloysite is a common pedogenic clay mineral, often found in young soils developed on volcanic deposits (Dixon, 1989), It is a member of the kaolin group of clays with the same ideal stoichiometric composition as kaolinite [Al2Si2O5(OH)4]. Halloysite, however, often contains water of hydration (i,e., Al2Si2O5(OH)4·nH2O), and is commonly found with a tubular morphology, This “rolling” of halloysite has received a great deal of study because there is no generally agreed upon mechanism for the process and there is no corresponding phenomenon in natural kaolinite (e.g. , Bates et al., 1950; Bailey, 1989; Singh, 1996; Singh and Mackinnon, 1996). The crystal structure of halloysite often shows stacking disorder. This property, combined with a rolled morphology, makes identification by X-ray diffraction (XRD) difficult. The XRD peaks at 7.5, 4.4, and 3.6 Å are often asymmetric with a large width at half peak height (Bailey, 1989).